The variegation on the stainless steel mesh belt not only affects the appearance, but also causes rust stains and affects the life of the equipment when used for a long time. Therefore, it is necessary to remove the variegation on the high-temperature mesh belt. How to remove, how to operate, what materials are needed. Here I will give you a detailed introduction to help you solve your confusion.
The first thing that needs to be prepared is industrial pickling cream, because it is very important to remove variegation with industrial pickling cream. Industrial pickling paste is mainly used to remove rust, oxide scale and welds on the surface of stainless steel, which can improve the appearance of stainless steel. Degreasing, pickling, and passivation can be completed at one time, the reaction speed is extremely fast, the removal is complete, and no spots are produced. Make the stainless steel surface get a uniform and beautiful silver white, improve the surface finish, and form a dense and complete passivation film with strong adhesion on the surface. The passivation film is generally 0.6-0.8 microns, and its breakdown potential can be increased. 100 millivolts, thereby improving the anti-corrosion performance of stainless steel products and prolonging the life of the equipment.
The method of removing the variegation of the high-temperature mesh belt is as follows:
Apply industrial pickling paste to the surface of the mesh belt with a thickness of 0.5-2mm.
Generally, the reaction time is 3-10 minutes or more, and it needs to be extended appropriately when it is used below 0°C or where the oxide scale is thick.
It is best to use a brush to scrub it several times during the treatment process. After the surface oxide scale is completely removed, rinse it with clean water (lime water or alkaline water is better) to avoid returning rust.
If there is clear water in the industrial pickling cream, do not pour it away, shake it well or stir well before use.
Wipe the surface of the mesh belt with a clean cloth.
After this treatment, the spots or rust spots on the mesh belt can be removed cleanly and the service life of the mesh belt can be improved. Knowing the operation method and the required materials, everyone can try to bring them to the product network for maintenance.